Ceramerplus is the higher oxidized material having a further enhanced thermal stability compared to Ceramer.
|
|
At 320 °C over a period of 12 hours the weight loss is less than 0.5% (curve d).
|
|
At 360 °C over a period of 12 hours the weight loss is about 1% (curve b).
|
|
The weight loss at the recommended pre- treatment temperature of 375 °C, for Ceramer, if Ceramer is used in free sintering of large volume parts is for Ceramerplus only 2% after 12 hours. The recommended pre-treatment temperature for Ceramerplus is just 120 - 160 °C.
|